Why does stainless steel mesh corrode and break

Rust steel mesh will not be corroded under normal conditions, but nothing **. Stainless steel mesh corrosion fracture is a corrosive fracture under the simultaneous action of stress and corrosion environment, generally speaking, stainless steel mesh in the corrosion environment, after external stress, will accelerate the speed of corrosion destruction.

The simple situation is the result of the superposition of these two elements, in a specific corrosion environment, when the metal material is not stressed, the corrosion damage is minimal, and when subjected to a certain stress, although the stress is sometimes far lower than the strength limit of the stainless steel mesh itself, after a period of time, so that the stainless steel mesh with good ductility will also break.

Such destruction is often carried out without warning, and the resulting destruction is severe and often catastrophic. There are roughly three necessary conditions for stress corrosion fracture, special environment, must be subjected to tensile force, stainless steel mesh itself is of poor quality.